Characterization of Asymmetric PES/SPSF Nanofiltration membranes |
Authors: Ma Feng1,2 Zhang Yu-zhong1,2 Ding Xiao-li1,2 Lin li-gang1,2 Li Hong1,2 |
Units: 1State Key Laboratory of Hollow Fiber Membrane Materials and Processes, Tianjin Polytechnic University, Tianjin 300106, China; 2School of Material Science and Engineering, Tianjin Polytechnic University, Tianjin 300160, China |
KeyWords: sulfonated polysulfone; polyethesulfone; nanofiltration; blend; asymmetric |
ClassificationCode:TQ028.8 |
year,volume(issue):pagination: 2012,32(1):46-50 |
Abstract: |
Polyethersulfone(PES)/Sulfonated polysulfone(SPSF) blend nanofiltration membranes were prepared using a simple phase inversion technique. The permeability of nanofiltration membranes fabricated with different sulfonation degree SPSF and SPSF contents was systematically studied. The results showed that nanofiltration membranes with PES/10% sulfonation degree SPSF ratio of 1.5 had high rejection of Na2SO4 (69%), NaCl(23.5%),PEG1000(99.8%), PEG800(81%) and,PEG600(57.8%) large pure water flux(90.3L/(m2h)) at 0.5MPa and 25℃. |
Funds: |
国家自然科学基金(50973083)、高等学校博士学科点专项科研基金(20091201120002),国家自然科学基金项目(50473025)。 |
AuthorIntro: |
马冯(1985—),男,湖南常德,硕士研究生,研究生期间从事纳滤膜的研究,E-mail:zzzzmama@163.com,通讯地址:天津市河东区成林道63号天津工业大学。张玉忠,E-mail:zhangyz2004cn@163.com。 |
Reference: |
[1] Yutaka Matsumoto. Preparation of composite UF membranes of sulfonated polysulfone coated on ceramics[J]. Journal of Membrane Science, 158 (1999) 55~62 [2] 环国兰,张宇峰,杜启云.纳滤复合膜的研制[J].水处理技术,2006.11(32):11~14 [3] X.J.Yang,A.G.Livingstion, L.Freitas dos Santos. Experimental observations of nanofiltration with organic solvents[J]. Journal of Membrane Science, 190 (2001) 45–55 [4] 丁礼琴,刘 力,徐德生.纳滤在制药及食品中的应用进展[J].中成药,2008.8(30):8~12 [5] Woei-Jye Lau, A.F. Ismail. Effect of SPEEK content on the morphological and electrical properties of PES/SPEEK blend nanofiltration membranes[J]. Desalination,249 (2009) 996–1005 [6] Noraaini Alia.The formation and characterisation of an asymmetric nanofiltration membrane for ammonia–nitrogen removal: Effect of shear rate[J]. Bioresource Technology, 101 (2010) 1459–1465 |
Service: |
【Download】【Collect】 |
《膜科学与技术》编辑部 Address: Bluestar building, 19 east beisanhuan road, chaoyang district, Beijing; 100029 Postal code; Telephone:010-80492417/010-80485372; Fax:010-80485372 ; Email:mkxyjs@163.com
京公网安备11011302000819号