湿法成型工艺制备碱性电池隔膜的研究
作者:申飞艳,张雄飞
单位: 长沙理工大学化学与生物工程学院
关键词: 聚丙烯纤维;棉纤维;碱性电池;电池隔膜
分类号: TS761.2
出版年,卷(期):页码: 2013,33(2):24-28

摘要:
以聚丙烯纤维和棉纤维为主要材料,采用湿法抄造的方法制备碱性电池隔膜材料。研究了打浆度对隔膜纸页性能的影响以及棉纤维、聚丙烯纤维的配比,分散剂、粘结剂等助剂,热压温度等因素对电池隔膜性能的影响。结果表明,采用70°SR的棉浆与聚丙烯纤维按1:2的质量配比,并添加1.0%的分散剂PEO以及6.0%的胶黏助剂PVA,在135℃的热压温度下可得到强度、吸碱性能良好的碱性电池隔膜,所得隔膜在电解质溶液中的电导率为3.38×10-2S•cm-1。
Alkaline batteries separator paper was prepared with polypropylene fiber and the 70°SR cotton fiber by wet papermaking. The influence of beating degree on the performance of the batteries separator paper was studied in this paper. And the influence of the quality ratio of polypropylene fiber and cotton fiber, the additives and hot-press temperature were also investigated in this paper. The results showed that, in the condition of 135℃ of hot pressing, adding PEO 1.0% and PVA 6.0% the performance of battery separator was best when the fiber ratio was 1:2. In electrolyte solution, the conductivity of separator was 3.38×10-2 S•cm-

基金项目:
湖南省科技攻关项目 (编号: 2008CK3073 ); 湖南省建设厅科研项目: (项目编号: 07hn j s002 )

作者简介:
张雄飞(1971.9——),男,湖南,博士,副教授,研究方向:能源材料,zxf0902@sina.com

参考文献:
[1]管从胜,杜爱玲,杨玉国.高能化学电源[M].北京:化学工业出版社,2005.
[2]吴立群,王安,李民,汪海,韩永强.碱性电池隔膜纸的研发及其发展趋势[J]. 中华纸业,2007,28(10):45—48.
[3]昊锋,毛立彩.碱性电池用准固态聚合物电解质膜[J]. 电池,2005,35(5):335—337.
[4]邓润荣. 高容量碱性电池隔膜纸的研究[J]. 电池工业,2007,12(5):303—306.
[5]陆燕华,王虹,余调娟,汤人望. 天丝纤谁在碱铭电沾隔膜中的应用研究[J]. 产业用纺织品,2010,28(9):14—21.
[6]许景秀,郭秉臣. 非织造布蓄电池隔膜材料及其工艺介绍[J]. 国际纺织导报,2002,(1):61—64.
[7]唐健,刘杰,安峰. 新型非织造材料在电池隔膜中的应用[J]. 产业用纺织品,2002,20(8):32—35.
[8]倪冰选,焦晓宁. 电池隔膜用聚丙烯非织造布改性研究[J]. 非织造布,2008,16(6):20—22.
[9]Yun-Feng Yang, Ling-Shu Wan, Zhi-Kang Xu. Surface hydrophilization of microporous polypropylene membrane by the interfacial crosslinking of polyethylenimine[J]. Journal of Membrane Science,2009,337:70—80.
[10]Yong-Hong Zhao, Kin-Ho Wee, Renbi Bai. Highly hydrophilic and low-protein-fouling polypropylene membrane prepared by surface modification with sulfobetaine-based zwitterionic polymer through a combined surface polymerization method[J]. Journal of Membrane Science,2010(362): 326—333.

服务与反馈:
文章下载】【加入收藏

《膜科学与技术》编辑部 地址:北京市朝阳区北三环东路19号蓝星大厦 邮政编码:100029 电话:010-80492417/010-80485372 传真:010-80485372邮箱:mkxyjs@163.com

京公网安备11011302000819号