| 海藻酸钙/明胶共混膜的制备及性能研究 |
| 作者：张君贤1，隋淑英1，朱平1，2，张林1，董朝红1，程文青1 |
| 单位： 1青岛大学“纤维新材料及现代纺织”国家重点实验室培育基地,山东青岛266071 |
| 关键词： 纤维素；丝素蛋白；溶解；复合膜 |
| 出版年,卷(期):页码： 2013,33(2):37-40 |
|
摘要： |
| 用蒸馏水溶解海藻酸钠和明胶，将两种溶液混合制得海藻酸钙/明胶复合功能膜，研究海藻酸钠/明胶复合共混膜的相容性、力学性能、透湿性及吸湿保湿性等。实验结果表明，明胶含量较少时，共混膜有良好的相容性和力学性能；海藻酸钙/明胶质量比为1:0.6时，共混膜的透湿性、吸湿保湿性较好。 |
| The composite film was prepared by alginate and gelatin which were both dissolved in distilled water. The characteristics of the composite film, such as, the compatibility, the mechanical property, the moisture absorption, the moisture retention and the moisture permeable property were analyzed in the study. The results showed that low content of gelatin lead to good compatibility, breaking strength and extension. And when the mass ratio was 1:0.6, the composite film had better moisture absorption, moisture retention and moisture permeable property. |
| 张君贤（1987-），男，山东青岛市人，青岛大学在读硕士研究生，研究方向为功能纤维及功能纺织品。E-mail:zhangjunxianlunwen@163.com 通讯作者：隋淑英（1960-），女，工学博士，青岛大学教授。研究方向为纺织材料的结构与性能。E-mail:sysui99@163.com |
|
参考文献： |
| [1] 张秀平,庄黎,宁霞,等.浅谈海藻纤维的开发和应用.[J].广西质量监督导报,2010,(4):52~53. [2] 郭肖青,朱平,王新,等.海藻纤维的制备及应用.[J].纺织导报,2006,(7):44~50. [3] 赵永霞.海藻纤维的发展及应用.[J].纺织导报,2008,(7):114~116. [4] 李承明,黄雅钦,黄明智.明胶在创伤敷料中的应用.[J].明胶科学与技术,2003,23(2):57~62. [5] 张宝钟,杜予民,樊李红,等.羧甲基壳聚糖/明胶共混膜的结构表征与吸湿保湿性.[J].分析科学学报,2005,21(3):245~248. [6] 马季铭,羌笛, 钟边笑,等.明胶凝胶表面润湿性的研究.[J].高等学校化学学报,1984,5(1):95~99. |
|
服务与反馈： |
| 【文章下载】【加入收藏】 |
《膜科学与技术》编辑部 地址：北京市朝阳区北三环东路19号蓝星大厦 邮政编码：100029 电话：010-64426130/64433466 传真：010-80485372邮箱：mkxyjs@163.com
京公网安备11011302000819号