NIPS法制备小孔径SPES-PES共混UF膜及其性能表征

作者：占琦伟¹，许振良¹，胡登¹，魏永明¹，江邦和²

单位： 1化学工程联合国家重点实验室，华东理工大学化学工程研究所膜科学与工程研发中心，上海200237； 2华东理工大学华昌聚合物有限公司，上海200237

关键词：磺化聚醚砜；聚醚砜；UF膜；非溶剂致相分离法

出版年,卷(期):页码： 2014,34(2):28-31

摘要：

采用非溶剂致相分离(NIPS，nonsolvent induced phase separation)法制备了小孔径磺化聚醚砜-聚醚砜（SPES-PES）共混超滤(UF)膜，对其进行了性能表征，讨论了溶剂、聚合物浓度、聚合物配比对膜性能的影响。结果表明，溶剂对膜性能的影响较大，用N,N-二甲基乙酰胺(DMAc)制得的UF膜通量和截留率相对来说都比较好；随着聚合物SPES-PES浓度的增大，水通量减小，对PEG10000的截留率先增大再基本保持不变；根据实验结果，共混UF膜的截留分子质量(MWCO)小于6000Da，其为负电荷小孔径共混UF膜。根据Matlab计算，共混UF膜的孔径为1.98nm，其MWCO为3060Da。

Sulfonated polyethersulfone(SPES)/polyethersulfone(PES) blend UF membrane with small pore size was prepared by the nonsolvent induced phase separation(NIPS) method, and the properties were also tested. The effects of solvents, concentration of polymers and the ratio of SPES to PES on membrane performance were considered. The result showed that the solvent had a huge impact on the membrane performance. The membrane made by dimethylacetamide (DMAc) had a better performance on flux and rejection. With an increasing of the concentration of polymers the flux of water decreased while the rejection of PEG-10000 increased first and then tended to be stable. The molecular-weight cut-off (MWCO) was under 6000Da, and the membrane was negatively charged blend UF membrane with small pore size by measuring the rejections of different solutions. On the basis of Matlab calculation, the pore size and MWCO of blend UF membrane were 1.98nm and 3060Da, respectively.

占琦伟(1982 ~)，女，湖北襄阳人，硕士研究生，研究方向为纳滤膜制备与应用等。*通信联系人：许振良，E-mail: chemxuzl@ecust.edu.cn；电话：021-64253061；传真：021-64252989

参考文献：

[1].Deng Hu, Zhen-Liang Xu, Chang Chen. Polypiperazine-amide nanofiltration membrane containing silica nanoparticles prepared by interfacial polymerization [J]. Desalination, 2012; 301:75-81
[2].Liu Jiu-Qng, Xu Zhen-Liang, Zhou Kang-Geng，Study on new method of the preparation of pure ammonium metatungstate (AMT) using a coupling process of neutralization- nanofiltration- nrystallization，J. Membr. Sci., 2004,240(1-2):1-9
[3].Ruihua Huang, Guohua Chen, Mingkun Sun, Congjie Gao.Preparation and characterization of composite NF membrane from a graft copolymer of trimethylallyl ammonium chloride onto chitosan by toluene diisocyanate cross-linking [J]. Desalination.2009, 239:38-45
[4].吕少丽，王红军，徐又一.聚醚砜超滤膜的亲水化改性研究进展[J]. 膜科学与技术. 2005，25（3）：80-84
[5].赵后昌，皇甫风云，白云东，孔媛媛，马琳. PSF/PES共混超滤膜的性能研究[J]. 化工新型材料. 2010，38（5）：97-101
[6].Wenying Shi，Benqiao He，Jianxin Li. Esterification of acidified oil with methanol by SPES/PES catalytic membrane[J]. Bioresource Technology，2011,102（9）：5389-5393
[7].Chalida Klaysorn, Bradley P. Ladewig, G. Q. Max Lu, Lianzhou Wang. Preparation and characterization of sulfonated polyethersulfone for cation-exchange membranes[J]. J. Membr. Sci. 2011，368:48-53
[8].李连超，马成良，谭惠民，陈天禄，徐纪平. 磺化聚醚酮复合纳滤膜的制备[J]. 水处理技术. 2005，31(10）:13-16
[9].李惠玲，谭翎燕，张浩勤，张永刚. 壳聚糖季铵盐/磺化聚醚砜复合纳滤膜的制备与表征[J]. 化工新型材料.2009，37(11):37-39
[10].Sarah Pouriafar，Ahmad Rahimpour，Mohsen Jahanshahi. Synthesis and characterization of PVA/PES thin film composite nanofiltration membrane modified with TiO2 nanoparticles for better performance and surface properties[J]. Journal of Industrial and Engineering Chemistry. 2012，18(4):1398-1405
[11].许振良，翟晓东，陈桂娥. 高空隙率聚偏氯乙烯中空纤维超滤膜的研究[J]. 膜科学与技术.2000，20(4):10-13
[12].李井峰. 相转化法制备聚醚砜微孔膜及其结构控制的研究[D]. 华东理工大学博士学位论文.上海. 2008
[13].谭翎燕，刘金盾，张浩勤，梁其辉.磺化聚醚砜（SPES）/聚砜（PSF）共混超滤膜的研制[J]. 化工进展. 2007, 26(6):864-868
[14].Qian Yang, Tai-Shung Chung, Y.E. Santoso. Tailoring pore size and pore size distribution of kidney dialysis hollow fiber membranes via dual-bath coagulation approach [J]. J. Membr. Sci. 2007，290:158-168

服务与反馈：

【文章下载】【加入收藏】

《膜科学与技术》编辑部地址：北京市朝阳区北三环东路19号蓝星大厦邮政编码：100029 电话：010-64426130/64433466 传真：010-80485372邮箱：mkxyjs@163.com