基于仿生机理的超疏水有机无机复合膜的制备

作者：韩鹏江春东周滢滢孙海翔栾延戈

单位：中国石油大学（华东）理学院材料物理与化学系，青岛 266555

关键词：超疏水膜；纳米二氧化硅；硅烷偶联剂；复合膜

出版年,卷(期):页码： 2015,35(2):25-29

摘要：

采用溶胶-凝胶法制备了纳米SiO2颗粒，并用低表面能硅烷偶联剂对其进行改性。改性后的SiO2粒子与聚偏氟乙烯（PVDF）按一定的质量比共混，利用相转化法制备了有机无机复合微孔膜。分析了偶联剂种类及SiO2粒径对微孔膜疏水性的影响，探讨了微孔膜表面能其疏水性能的影响，并对复合膜的微观形貌进行了表征。研究结果表明：硅烷偶联剂可以有效阻止SiO2溶胶的凝胶作用，降低SiO2的表面能，而表面能对膜的疏水性有显著的影响；制备的复合微孔膜具有良好的微纳米阶层结构，疏水角达到了151°。

Organic-inorganic composite microporous membrane was fabricated by phase inversion after PVDF mixed with modified SiO2 according to a weight ratio, in which SiO2 prepared by sol-gel method was modified by low-surface-energy silane coupling agent. The impact of coupling agent types and SiO2 particles size on the hydrophobicity of the microporous film and the microtopography of the film were investigated. Results indicated that the gelation of SiO2 particles were effectively prevented by silane coupling agent with surface energy of SiO2 particles reduced, which had a significant impact on hydrophobicity of membrane; the water contact angle of the composite microporous membrane surfaces with a nicer micro-nano hierarchical structure was up to 151°.

韩鹏（1992-），男，山东济南人，本科生，主要从事高分子膜分离研究。

参考文献：

[1] Cassie A B D, Baxter S. Wettability of porous surfaces [J]. Trans Faraday Soc, 1944, 40: 546-551.
[2] Hou X, Jiang L. Learning from nature: building bio-inspired smart nanochannels [J]. ACS Nano, 2009, 11: 3339-3342.
[3] Bhushan B, Jung Y C, Koch K. Self- cleaning efficiency of artificial superhydro- phobic surfaces [J]. Langmuir, 2009, 25: 3240-3248.
[4] 王庐岩, 钱英, 刘淑秀, 等. 聚偏氟乙烯分离膜改性研究进展[J]. 膜科学与技术，2002, 22(5): 52-57.
[5] Bhushan B, Ling X. Integrating elec -trowetting into micromanipulation of liquid droplets [J]. J Phys Condens Matter 2008, 20: 1-10.
[6] Nosonovsky M, Bhushan B. Superhydro- phobicity for energy conversion and nservation applications [J]., J Adhes Sci Technol 2008, 22: 2105-2115.
[7] Öner D, Mccarthy T J. Ultrahydrophobic surfaces: Effects of topography length scales on wettability [J]. Langmuir 2000, 16: 7777-7782.
[8] Liu H, Feng L, Zhai J, et al. Reversible wettability of a chemical vapor deposition prepared ZnO film between superhydrophobicity and superhydrophilicity [J]. Langmuir 2004 20: 5659-5661.
[9] Neinhuis C, Barthlott W. Characte- rization and distribution of water-repellent, self-cleaning plant surfaces [J]. Ann Bot 1997, 79: 667-677.
[10] 张裕卿, 张红柳, 曲云, 等. 填充纳米SiO2 对聚偏氟乙烯膜性能的影响 [J].膜科学与技术, 2007,27 (6): 47-51.
[11] Sethupathy M, Sethuraman V, Manisanker P. Preparation of PVDF/SiO2 Composite Nanofiber Membrane Using Electrospinning for Polymer Electrolyte Analysis[J]. Soft Nanoscience Letters, 2013, 3, 37-43.
[12] 张华峰, 张玉忠, 林立刚, 等. PVDF膜的制备与疏水性研究[C]. 第四届中国膜科学与技术报告会论文集. 中国北京: 《膜科学与技术》编辑部, 2010. 240-242.

服务与反馈：

【文章下载】【加入收藏】

《膜科学与技术》编辑部地址：北京市朝阳区北三环东路19号蓝星大厦邮政编码：100029 电话：010-64426130/64433466 传真：010-80485372邮箱：mkxyjs@163.com