磺化热压PPS非织毡的性能研究
作者:徐志成,王乐译,张伟政,赵岳轩,万思青,王新艳
单位: 山东招金膜天有限责任公司,招远 265400
关键词: PPS;磺化反应;亲水性;离子交换能力
分类号:
出版年,卷(期):页码: 2015,35(3):98-101

摘要:
 利用磺化反应及热压处理改善聚苯硫醚(PPS)非织毡的亲水性和离子交换能力,讨论了时间、温度、热压压力等不同反应条件对PPS亲水性及离子交换能力的影
响。实验结果表明,在磺化反应温度为80℃,反应时间为1.5h的磺化反应条件及热压压力为9Mp条件下,不仅PPS非织毡的亲水性和离子交换能力得到了显著的改善,同时还保留了较好的力学性能和耐腐蚀性。
 
 The hydrophilic property and ion-exchange capacity of PPS non—woven felt were improved by using sulphuration and hot-pressed technique. The effects of time,temperature and the ratio of reactants on the hydrophilic property and ion-exchange capacity of PPS were illustrated in detail.The results show that not only the hydrophilic property and ion-exchange capacity of PPS non—woven felt are excellently improved, but also the original stretch intensity and corrosion resistance of PPS non—woven felt are well retained when the sulphuration temperature is 80 ℃,time is 1.5 h and hot-pressed pressure is 9Mp .
 

基金项目:
国家科技支撑计划(2014BAK13B02)

作者简介:
徐志成(1980-),男,山东潍坊人,硕士,工程师,从事高分子膜制备与应用方向研究

参考文献:
[1]郭振华.对我国PPS开发之我见[J].化工新型材料,1995,(5):26—30.
[2]富醇熹.双向拉伸PPS薄膜[J].化工新型材料,1993,(2):36,38.
[3]陈贻炽.聚苯硫醚的合成及性能[J].化工新型材料,1994,(8):2l一24.
[4]张念萱,刘皓颖.PPS双向拉伸膜发展概况[j].北京化工,1994,(3):l3一l7.
[5]杨淑丽.改性聚苯硫醚的性能和应用[J].塑料技术,1997,7(2):4—9.
[6]崔小明.聚苯硫醚的生产应用与市场前景[J].合成材料老化与应用,2001,(4):40—41.
[7] 祝振鑫. 膜材料的亲水性、膜表面对水的湿润性和水接触角的关系[J].膜科学与技术,2014 ,34(2):1-4.

服务与反馈:
文章下载】【加入收藏

《膜科学与技术》编辑部 地址:北京市朝阳区北三环东路19号蓝星大厦 邮政编码:100029 电话:010-80492417/010-80485372 传真:010-80485372邮箱:mkxyjs@163.com

京公网安备11011302000819号