粘胶纤维行业碱回收工艺中纳滤膜的清洗研究

作者：姚萌方永珍朱丽香洪昱斌

单位：三达膜科技(厦门)有限公司,厦门 361022

关键词：纳滤膜；碱回收；膜污染；膜清洗

出版年,卷(期):页码： 2016,36(3):115-117

摘要：

粘胶纤维生产过程中产生含油溶解性半纤维素的浓碱液，应用耐碱纳滤膜过滤技术，实现NaOH与半纤维素分离，可达到回收碱液的目的。本项目工艺选用型号Suntar-357卷式复合耐碱膜，其正常运行通量为23 LMH，经过长期运行膜污染后，通量下降>60 %。将膜芯剖开，通过酸碱溶解实验、丁达尔实验分析污染物为胶体类物质。选用LC-01、LC-90、LC-42清洗剂，其中，LC-42号清洗剂效果最佳，其膜通量恢复率分别为52.2 %、60.9 %、73 %、90.4 %。经过逐步清洗，膜过滤通量恢复率为90 %。

Concentrated alkali was generated during viscose fiber industry. Nanofiltration membrane was used to separate NaOH and semi cellulose. Suntar-357 nanofiltration membrane was applied in this project. The normal membrane flux was 23 LMH. After a long-term operation, the flux declined >60 %. The fouling substances were tested as colloidal substances by alkali dissolution experiment and of Dindar experiment. LC-01, LC-90 and LC-42 were used as the cleaning agent. The LC-42 agent was the best. The water flux recovery was 52.2 %, 60.9 %, 73 %, 90.4 %, respectively. The water flux recovery was 90.4%.

作者简介：姚萌（1982～），女，河北人，博士，工程师，三达膜科技（厦门）有限公司，主要研究方向为膜技术应用，E-mail：yaom@suntar.com

参考文献：

[1] 田晴, 陈季华.纺织粘胶黑液污染及治理. [J]. 化工环保, 2004, 24: 151-153.
[2] 周正华. 我国粘胶纤维的现状及发展前景. [J]. 苏州大学学报：工科版, 2004, 24(6): 52-54.
[3] 程虎得, 张小泉. 粘胶纤维生产废水处理运行工艺控制. [J]. 人造纤维, 2015, 45(1).
[4] 李岩. 纳滤膜技术在造纸黑液中废碱液回用的研究. [D]: [学位论文]. 吉林大学, 2011. 25-26
[5] 张化文. 粘胶纤维废碱液纳滤回收装置技术运行分析. [J]. 绿色科技, 2013(6): 214-216.
[6] 严滨, 於锦锋, 吴发辉, 等. 纳滤技术在制药业废碱回收中的应用研究. [J]. 厦门理工学院学报, 2009, 17(1): 22-26.
[7] 刘志龙, 赵民. 红霉素发酵液纳滤膜污染与再生. [J]. 膜科学与技术, 2014, 34(1): 116-120.

服务与反馈：

【文章下载】【加入收藏】

《膜科学与技术》编辑部地址：北京市朝阳区北三环东路19号蓝星大厦邮政编码：100029 电话：010-64426130/64433466 传真：010-80485372邮箱：mkxyjs@163.com