氯磺酸磺化PPS非织毡薄膜及表征

作者：徐志成，王乐译，张伟政，赵岳轩

单位：山东招金膜天有限责任公司，招远 265400

关键词： PPS；磺化反应；亲水性

出版年,卷(期):页码： 2016,36(5):68-71

摘要：

利用磺化反应改善聚苯硫醚(PPS)非织毡薄膜的亲水性，讨论了时间、温度等不同反应条件对磺化反应的影响。磺化后PPS表面—SO3H基团的引入可由红外光谱（FTIR）及X光量子能谱（EDX）数据得到确认，在KYKY型电子显微镜下观察了纤维微观形貌。实验结果表明，在反应温度为80℃，反应时间为1.5 h的磺化反应条件下，不仅PPS非织薄膜的亲水性得到了显著的改善，同时还保留了较好的力学性能。

The hydrophilic property of PPS non—woven felt thin film was improved by using sulphuration.The effects of time，temperature and the ratio of reactants on the property of hydrophilic of PPS were illustrated in detail．The introduction of —SO3H to sulphurated PPS was characterized by FTIR spectroscopy and Energy Dispersive X-ray (EDX). The result shows that not only the hydrophilic property of PPS non—woven felt is excellently improved but also the original stretch intensity of PPS non—woven felt thin film is well retained when the sulphuration temperature is 80℃ and time is 1.5 h．

作者简介：徐志成（1980-），男，山东潍坊市人，硕士研究生，工程师，从事高分子膜制备与应用方向研究；电子邮件：chenggong-2100@163.com

参考文献：

[1]郭振华，对我国PPS开发之我见[J]．化工新型材料，1995，(5)：26—30．
[2]富醇熹．双向拉伸PPS薄膜[J]．化工新型材料，1993，(2)：36，38．
[3]陈贻炽．聚苯硫醚的合成及性能[J]．化工新型材料，1994，(8)：2l一24．
[4]张念萱，刘皓颖．PPS双向拉伸膜发展概况[j]．北京化工，1994，(3)：l3一l7．
[5] 余建佳，李飞，周璇. 磺化聚苯醚的制备[J],胶体与聚合物,2005,23：22-23
[6]陈雷,张俊,杨昌正等. 磺化SBS 薄膜的制备与表征[J]，功能高分子学报,1998 ,11(1):39-43.
[7]吕亮,许青青.废旧聚苯乙烯磺化反应研究[J],天津化工,2002,5：11-12.
[8]韦异,陈薇,赵文锋等.SBS的磺化改性[J],精细石油化工,2002,5：23-25.
[9]KIMIC,TAKTM,CHOIJG.Sulfonated polyether-sulfone by heterogeneous method and its membraneperformances[J],J Appl Polym Sci,1999,74(8)：2046- 2055.
[10]项昭保,霍丹群,候长军等.聚醚砜的磺化改性[J],重庆大学学报,2002,25(10)：117-120.

服务与反馈：

【文章下载】【加入收藏】

《膜科学与技术》编辑部地址：北京市朝阳区北三环东路19号蓝星大厦邮政编码：100029 电话：010-64426130/64433466 传真：010-80485372邮箱：mkxyjs@163.com