煤基管状微滤炭膜的增强改性

作者：宋学凯，王同华，张万栋，姜华玮，张煜，董军营

单位：大连理工大学，精细化工国家重点实验室，炭素材料研究实验室，

关键词：煤，炭膜，炭纤维，增强

出版年,卷(期):页码： 2011,31(1):51-55

摘要：

针对微滤炭膜机械强度的不足，采用在煤中加入炭纤维增强材料和调控不同煤种的比例关系的方法对其进行机械强度的增强改性。结果表明，在无烟煤基炭膜中加入炭纤维对其机械强度的改善效果不明显。而同时加入粘结性烟煤可明显地改善炭膜的机械强度，并随着炭纤维加入量的提高炭膜的抗冲击强度增加显著，但径向抗压强度略有降低。通过调控不同煤种的比例关系也可明显地提高炭膜的机械强度。扫描电镜分析发现，粘结性烟煤的加入改善了炭纤维和炭膜基体的复合效果，炭纤维在炭膜中沿炭膜长度方向取向分布。

The mechanical strengths of coal-based tubular microfiltration carbon membranes were modified and enhanced by means of adding carbon fiber and controlling the ratio of different coals. The results showed that the improvement of mechanical strengths was not obvious by adding carbon fiber in anthracite-based carbon membranes, but the mechanical strengths of carbon membranes could significantly be improved by adding some carbon fiber and caking coal in anthracite-based carbon membranes at the same time. The impact strength increased greatly and radial compressive strength decreased slightly with the increase of quantity of carbon fiber added in carbon membrane. The mechanical strengths of carbon membranes could also be improved obviously by controlling the ratio of different coals. The images of SEM indicated that addition of caking coal could improve the composite effect of carbon fiber and carbon membranes, and carbon fibers showed orientation distribution along with the length of carbon membrane

宋学凯(1983- )，男，山东省人，硕士生，从事炭材料和膜材料的研究。

参考文献：

[1] 王同华,魏巍,刘淑琴等.管状多孔炭膜的研究[J].新型炭材料,2000,15(1):6-11.
[2] 王同华,刘淑琴,尤隆渤.煤基管状炭膜支撑体的研究(I)原料性质对支撑体孔结构性能的影响[J].煤炭转化,1998,21(3):73-76.
[3] ISmail A F,David L I B.A review on the latest development of carbon membranes for gas separation [J].J Membr Sci,2001,193:1-18.
[4] Saufi S M,Ismail A F.Fabrication of carbon membranes for gas separation––a review [J].Carbon,2004,42:241-259.
[5] Teresa A. Centeno,Antonio B.Fuertes. Supported carbon molecular sieve membranes based on a phenolic resin.J Membr Sci,1999,160：201-211.
[6] H.H.Schobertm, C.Song,Chemicals and materials from coal in the 21st century [J].Fuel,2002,81: 15-32.
[7] 虞继舜,戴中蜀,何选明.煤化学[M].北京 :冶金工业出版社,2000 :5-86.
[8] 潘艳秋,李凤延,张威等.气液两相流在炭膜微滤钛白悬浮液中的应用研究[J].高校化学工程学报,2009,23(1):34-38.
[9] 潘艳秋,李红剑,王同华等. 炭膜处理含油污水的实验研究[J]. 高校化学工程学报,2004, 18(1):13-16.
[10] 王细凤,潘艳秋,王同华.炭膜处理含油废水的研究[J].膜科学与技术,2001,21(6):59- 62.
[11] Song Chengwen, Wang Tonghua, Pan Yangqiu, Preparation of coal-based microfiltration carbon membrane and application in oily wastewater treatment. Separation and Purification Technology, 2006,51:80-84.
[12] 王芳,杨凤林,宫正等. 炭管膜曝气生物膜反应器SNAD脱氮研究[J].环境工程学报,2009, 3(3):405-408.
[13] 孙翠,杨凤林,胡绍伟等.炭管曝气膜强化厌氧折流板反应器功能的研究[J].环境科学, 2008,29(5):1216-1220.
[14] 刘惠军,杨凤林,张捍民等.炭膜曝气生物膜反应器硝化作用及其微生物群落结构分析[J].环境科学,2007,28(9):2123-2128.
[15] 王同华,宋成文.一种煤基炭膜的制备方法:中国,CN1490076[P].2004.04.21.
[16] 王同华,宋成文.一种煤基炭膜的调孔方法:中国,CN1490075[P].2004.04.21.
[17] Venkataraman K, Choate W T, Torre E R et al. Characterization studies of ceramic membranes : a novel technique using a coulter porometer [J].J. Membr.Sci, 1988,39:259-265.
[18] 王同华,宋成文. 一种多孔无机膜的孔径分布测定装置中膜池的结构:中国,CN2643317 [P].2004.09.22.

服务与反馈：

【文章下载】【加入收藏】

《膜科学与技术》编辑部地址：北京市朝阳区北三环东路19号蓝星大厦邮政编码：100029 电话：010-64426130/64433466 传真：010-80485372邮箱：mkxyjs@163.com