催化与PV双功能中空纤维复合膜制备及其应用过程

作者：许振良，马晓华，魏永明，程亮

单位：华东理工大学化学工程联合国家重点实验室，化学工程研究所膜科学与工程研发中心

关键词：中空纤维复合膜，规整填料，催化精馏，渗透汽化

出版年,卷(期):页码： 2011,31(3):210-215

摘要：

本文以聚丙烯腈（PAN）中空纤维膜为支撑底膜，聚乙烯醇（PVA）为渗透汽化(PV)层，全氟磺酸树脂(PFSA)-聚乙烯醇(PVA)-纳米材料(SiO2、Al2O3和TiO2)为催化层，制备了具有催化和PV双功能的PFSA-PVA-SiO2(Al2O3和TiO2)/PVA/ PAN中空纤维复合膜。以乙酸-乙醇酯化反应塔顶粗酯考察其分离性能，以乙酸-乙醇酯化反应考察其催化性能，同时还考察了分离膜作为规整填料的精馏性能。实验结果表明：催化层和PV层能紧密粘结在底膜上，具有良好的PV性能，其渗透通量约170 g/m2 h，对乙醇的选择性高于27，且无乙酸乙酯透过，以及具有良好的催化性能；当复合膜用作规整精馏填料时，与传统精馏填料相比，能显著降低HTU（小于10cm）；与文献中的中空纤维膜规整填料相比，气液在膜的管层、壳层分开与否对HTU影响不大。

Difunctional hollow fiber composite membranes (PFSA-PVA-SiO2 (Al2O3 and TiO2)/PVA/PAN) with catalysis and pervaporation (PV) were prepared, in which employed PAN as support membrane, PVA as separative layer, and PFSA-PVA-nanoparticles (SiO2, Al2O3 and TiO2) as catalytic layer. The separation performances of difunctional membranes were investigated by dehydrating the top product of ethanol-acetic acid esterifiaction reaction, the catalytic activities of them were studied through ethanol-acetic acid esterification reaction, and the distillation performances of single functional pervaporation membranes as structural packings were explored by separation ethanol-water solution. The results showed that both of the separative and catalytic layers were coated on the PAN support membrane tightly; the difunctional membranes had remarkably separation performances in terms of permeation fluxes (approximately 170 g/m2 h) and separation factors (separation factors of water to ethanol were all higher than 27, and no ethyl acetate permeated); the difunctional membranes had good catalytic activities and the ethanol-acetic acid esterification conversion could reach to 56.5% when using them as catalyst. When used single functional pervaporation membranes as structural packings in distillation, the HTU was decreased significantly (lower than 10cm) compared with conventional distillation packings, and the gas and liquid on either side of the hollow fiber (tube side or shell side, in literatures) or both on the shell side (in this experiment) had little influences on HTU.

许振良(1962 ~)，男，江苏江阴市人，教授、博导，主要研究膜科学与工程、分离科学与工程、污水治理工程等。

参考文献：

[1]. 林兰, 张国亮, 孟琴等. 用于醇-水体系分离技术的研究进展[J]. 化工进展, 2007, 27(3): 362-367.
[2]. Zhang G, Cussler E L. Distillation in hollow fibers [J]. AIChE J, 2003, 49(9): 2344-2351.
[3]. Zhang G, Cussler E L. Hollow fibers as structured distillation packing [J]. J Membr Sci, 2003, 215(1-2): 185-193.
[4]. Chung J B, DeRoche r J P, Cussler E L. Distillation with nanoporous or coated hollow fibers [J]. J Membr Sci, 2005, 257(1-2): 3-10.
[5]. Yang Dali, Barbero Robert S, Devlin David J, Cussler E L. et al. Hollow ?bers as structured packing for olefin/paraffin separations [J]. J Membr Sci，2006, 279: 61-69.
[6]. Zhang G, Lin L, Meng Q, et al. Distillation o f methanol-water solution in hollow fibers [J]. Sep & Purif Techn, 2007, 56(2): 143-149.
[7]. Zhang G, Lin L, Meng Q, et al. Separation of alcohol-water solutions by distillation through hollow fibers [J]. Ind Eng Chem Res, 2007, 46(23): 7820-7825.
[8]. 张国亮，孙海敏，陈银飞，何晋浙. 精馏分离中的新型中空纤维膜结构填料及其传递现象[J]. 高校化学工程学报, 2008, 22(2): 223-228.
[9]. 许振良，郎万中，童蔚，石卫，由废弃全氟离子膜制备全氟磺酸树脂溶液的方法，中国发明申请号：CN200510025801.4 (2005.05.13); 公开号: CN1699450A(2005.11.23); 授权专利号: ZL200510025801.4(2006.11.8)
[10]. Xiao-Hua Ma, Zhen-Liang Xu, Yang Liu, De Sun, Preparation and characterization of PFSA-PVA-SiO2/PVA/PAN difunctional hollow fiber composite membranes [J]. J Membr Sci, 2010, 360: 315-322.
[11]. Hai-Kuan Yuan, Zhen-Liang Xu, Jiang-Huan Shi, Xiao-Hua Ma, Perfluorosulfonic Acid -Tetraethoxysilane/Polyacrylonitrile (PFSA-TEOS/PAN) Hollow Fiber Composite Membranes Prepared for Pervaporation Dehydration of Ethyl Acetate-Water Solutions. J Appl Polym Sci, 2008, 109(6): 4025-4035.

服务与反馈：

【文章下载】【加入收藏】

《膜科学与技术》编辑部地址：北京市朝阳区北三环东路19号蓝星大厦邮政编码：100029 电话：010-64426130/64433466 传真：010-80485372邮箱：mkxyjs@163.com