高通量自清洁多孔PZT压电陶瓷膜的制备

作者：卜佳伟，毛恒洋，邱鸣慧，范益群

单位：南京工业大学化工学院，材料化学工程国家重点实验室，南京 210009

关键词：压电陶瓷；膜分离；膜污染；自清洁；含油乳化液

出版年,卷(期):页码： 2020,40(1):72-77

摘要：

以PbZr0.52Ti0.48O3(PZT)压电陶瓷粉体为原料，淀粉为造孔剂，通过干压成型法制备多孔PZT压电陶瓷膜，考察了造孔剂含量对多孔PZT压电陶瓷膜微结构及压电性能的影响.结果表明，随着造孔剂含量的增加，陶瓷膜的孔隙率和纯水渗透率逐步增加，而机械强度和压电性能逐步降低.当加入2.5%的造孔剂时，多孔陶瓷膜纯水渗透率为2250 L·m-2·h-1·MPa-1，最可几孔径为0.5 μm左右，极化后可产生振幅为42 mV的振动信号.将此条件下制备得到的多孔PZT压电陶瓷膜在含油乳化液中进行过滤实验，发现陶瓷膜无超声作用时，其通量迅速衰减至初始通量的37%.而在原位超声作用下，陶瓷膜通量衰减缓慢，并且稳定在55%左右，表明PZT压电陶瓷膜产生的超声起到了抗污染的效果.

Porous lead zirconate titanate (PZT) ceramic membranes were fabricated with starch as pore-forming agent. Effects of starch content on microstructure and piezoelectric performance of membranes were studied. The results show that the porosity and pure water permeability of the ceramic membrane increase with the increasing of the pore-forming agent, while the mechanical strength and piezoelectric properties are gradually decreased. When 2.5% pore-forming agent is added, the water permeability of ceramic membrane is 2250 L·m-2·h-1·MPa -1, the pore size is about 500 nm, and the resonance amplitude signal is 42 mV. The optimized PZT membrane was applied in oil-in-water emulsion wastewater purification to test its self-cleaning performance. With in-situ ultrasound, the stationary permeability of PZT membrane was 55% of its initial value while this value was 37% as opposed to without. This demonstrated the self-cleaning performance of the ultrasound generated by PZT membrane.

第一作者简介：卜佳伟（1994-），男，山西晋中人，硕士，从事膜分离材料的研究与应用.*通讯作者，E-mail：qiumh_1201@njtech.edu.cn

参考文献：

[1] Kang G, Cao Y. Application and modification of poly(vinylidene fluoride) (PVDF) membranes - A review[J]. J Membr Sci, 2014, 463: 145-165.
[2] Zhang R, Liu Y, He M, et al. Antifouling membranes for sustainable water purification: strategies and mechanisms[J]. Chem Soc Rev, 2016, 45(21): 5888-5924.
[3] 范益群, 邢卫红. 陶瓷膜表面性质研究进展[J]. 膜科学与技术, 2013, 33(05): 1-7.
[4] Gao N, Li M, Jing W, et al. Improving the filtration performance of ZrO2 membrane in non-polar organic solvents by surface hydrophobic modification[J]. J Membr Sci, 2011, 375(1-2): 276-283.
[5] Gonzalez-Avila SR, Prabowo F, Kumar A, et al. Improved ultrasonic cleaning of membranes with tandem frequency excitation[J]. J Membr Sci, 2012, 415: 776-783.
[6] Coster HGL, Farahani TD, Chilcott TC. Production and characterization of piezo-electric membranes[J]. Desalination, 2011, 283: 52-57.
[7] Darestani MT, Coster HGL, Chilcott TC, et al. Piezoelectric membranes for separation processes: Fabrication and piezoelectric properties[J]. J Membr Sci, 2013, 434: 184-192.
[8] Darestani MT, Chilcott TC, Coster HGL. Changing the microstructure of membranes using an intense electric field: Filtration performance[J]. J Membr Sci, 2014, 449: 158-168.
[9] Krinks J K, Qiu M H, Mergos I A, et al. Piezoceramic membrane with built-in ultrasonic defouling[J]. J Membr Sci, 2015, 494: 130-135.
[10] 毛恒洋, 邱鸣慧, 范益群. 多孔PZT压电陶瓷膜的制备及其抗污染性能[J]. 化工学报, 2017, 68(03): 1224-1230+1794.
[11] Zou D, Qiu M H, Chen X F, et al. One-step preparation of high-performance bilayer alpha-alumina ultrafiltration membranes via co-sintering process[J]. J Membr Sci, 2017, 524: 141-150.
[12] Feng J, Qiu M H, Fan Y Q, et al. The effect of membrane thickness on the co-sintering process of bi-layer ZrO2/Al2O3 membrane[J]. J Membr Sci, 2007, 305(1-2): 20-26.
[13] Aust U, Benfer S, Dietze M, et al. Development of microporous ceramic membranes in the system TiO2/ZrO2[J]. J Membr Sci, 2006, 281(1-2): 463-471.
[14] Obada D, Dodoo A, Dauda M, et al. Physico-mechanical and gas permeability characteristics of kaolin based ceramic membranes prepared with a new pore-forming agent[J]. Appl Clay Sci, 2017, 150: 175-183.
[15] 张松林, 徐卓, 李振荣, 等. 造孔剂含量对多孔BiScO3-PbTiO3高温压电陶瓷性能的影响[J]. 材料科学与工艺, 2016, 24(05): 9-13.
[16] Mao H Y, Qiu M H, Bu J W, et al. Self-cleaning piezoelectric membrane for oil-in-water separation[J]. Acs Appl Mater Inter, 2018, 10: 18093-18103.
[17] Mao H Y, Bu J W, Qiu M H, et al. PZT/Ti composite piezoceramic membranes for liquid filtration: Fabrication and self-cleaning properties[J]. J Membr Sci, 2019, 581: 28-37.

服务与反馈：

【文章下载】【加入收藏】

《膜科学与技术》编辑部地址：北京市朝阳区北三环东路19号蓝星大厦邮政编码：100029 电话：010-64426130/64433466 传真：010-80485372邮箱：mkxyjs@163.com